Analysis of the failure causes in the flattening test of 2205 duplex stainless steel seamless tubes
•Employed industrial CT scanning to investigate crack defects in 2205 duplex stainless steel seamless pipes.•Identified large-sized CaO-Al2O3-MgO inclusions as the root cause of crack initiation and propagation.•Demonstrated the novel application of industrial CT for non-destructive evaluation.•Prop...