Effect of Cyclic Load Frequency on the Fatigue Crack Nucleation and Growth of Annealed and Prestrained Austenitic SS 304 - Nascimento, Brenno L.; Santos, Iris S.; Santos, Luiara L.; Reis, Matheus M. S.; Jesus, Ihana G. C.; Griza, Sandro (Fatigue & fracture of engineering materials & structures, 2025)
Keywords: austenitic SS 304; Austenitic stainless steels; Corrosion effects; Corrosion fatigue; Crack initiation; Cyclic loads; Ductility tests; Edge dislocations; fatigue; Fatigue cracks; Fatigue failure; Fatigue strength; Fatigue tests; Fracture mechanics; Heat resistant steels; Load; load frequency; Martensite; Metal fatigue; Nucleation; Performance evaluation; Plastic deformation; Stainless steel; Strain analysis; Thermal stability