Evaluation of mechanical characteristics of 3003 aluminum alloy plated sheets

• Published in: IOP conference series. Materials Science and Engineering Vol. 1262; no. 1; pp. 12022 - 12036
• Main Authors: Lazar (Natra), C, Istrate, D, Odagiu, O P, Demian, A M, Buzatu, A D, Ghiban, B
• Format: Journal Article
• Language: English
• Published: Bristol IOP Publishing 01.10.2022
• Subjects: Alloys; Aluminum base alloys; Capability indices; Comparative analysis; Control charts; Control limits; Elongation; Heat exchangers; Mechanical properties; Melting points; Normal distribution; Performance indices; Radiators; Sheets; Stability analysis; Statistical analysis; Thickness; Weight reduction
• ISSN: 1757-8981; 1757-899X
• DOI: 10.1088/1757-899X/1262/1/012022

Aluminum based alloys are widely used as applications for heat exchangers, especially for car radiators. The main alloy used is 3003 (in according with ISO6361), which is usually plated with a 4000 series alloy (which has a lower melting point). The present paper gives a comparative analysis of the mechanical characteristics values of the 3003 alloy plated sheets, in different states (state O and state H24), and different sheet thicknesses (0.5 mm, 0.97 mm, and 2 mm respectively). Statistical comparative analysis shows that the considered processes are stable (in control) in the sense of control chart (X chart and R chart values) are within the control limits and there are no specific trends. The stability of the processes was highlighted by the use of performance indices. Thus, the C PK performance index in all the analyzed situations is much higher than 1.33, which means that the processes are stable with a normal distribution of values. Instead, the P PK capability index values are much lower than C PK . The distribution of elongation values (in state O, at a thickness of 0.97 mm - with the value of the P PK capability index 1.95 and in state O 2.5 mm thickness - with the value of the P PK capacity index 2.25 mm) has a value greater than 1.67, which indicates that this characteristic is in a state of statistical control (ie P PK ≥ 1.67 and C PK ≥ 1.33). The fact that for the other characteristics the value of the P PK ≤ 1.67 capability index, and yet the process is stable, means that there must be process improvements through various corrective measures until continuous stability is achieved. The complete statistical analysis, performed on the values of the mechanical characteristics, of the 3003 alloy plated sheets, in different delivery states and different thicknesses, showed, finally, that the applied technological processes led to obtaining appropriate mechanical characteristics, without deviating from outside the limits of tolerance, with high reproducibility and stability.